Why

250um tire vulcanization label

Excellent high-temperature stability, capable of enduring the heat and pressure (up to 210℃) during tire usage and vulcanization with sulfur.

Outstanding durability and wear resistance.

Excellent chemical resistance: Strong waterproofing, resistant to acids, salts, alkalis, most petroleum stains, oils, and low-fat solvents. The adhesive can penetrate into concave surfaces, firmly bonding with the softener that penetrates out of the tire surface. When the vehicle is in operation, the barcode will not fall off spontaneously, and forced manual peeling will not damage the rubber on the tire surface.

Excellent barcode/thermal transfer printing effect, combined with XiYan VR-30 ribbon, ensuring 100% accurate scanning and reading on high-speed conveyors before and after vulcanization.

Excellent conformability: When the tire is removed from the mold, the strong flexibility can withstand tire deformation.

Physical Properties Test Method Average Test Results
Thickness ASTM D1000 Test US Units SI Units
Base Material 0.0098 in 0.250 mm
Adhesive 0.0010 in 0.026 mm
Total 0.0108 in 0.276 mm
Initial Tack (Adhesion to Steel Ball) ASTM D3759 Test Approximately equivalent to a 3# steel ball
Adhesion Duration: FTM8 Test ＞12 hours
Temperature Range -40 to 428°F (-40~220°C)
Shelf Life 1 year at 73.4°F (23°C) and 60% relative humidity
UL File Number To be determined
UL Test Ribbon OwnLikes VR-30

 

 

 

 

 

 

 

 

 

All SI units are calculated from US customary units.

Why

188um bright white rubber vulcanization label

Excellent high-temperature stability, enduring the heat and pressure (up to 210℃) during tire usage and sulfur treatment.

Outstanding durability and resistance to wear.

Excellent chemical resistance: Strong waterproofing, resistant to acids, salts, alkalis, most petroleum stains, oils, and low-fat solvents. The adhesive can penetrate into concave surfaces, firmly bonding with the softening agent that seeps out of the tire surface. This ensures that the barcode does not fall off spontaneously during vehicle operation, and forced removal by humans will not damage the tire's rubber surface.

Exceptional barcode/thermal transfer printing effect, combined with XiYan VR-30 ribbon, ensuring 100% accurate scanning and reading on high-speed conveyor lines before and after vulcanization.

Excellent conformability: When the tire is removed from the mold, its strong flexibility accommodates tire deformation.

Physical Properties Test Method Average Test Results
Thickness ASTM D1000 Test US Units Standard Units
Base Material 0.0074in 0.188mm
Adhesive 0.0010in 0.026mm
Total 0.0084in 0.214mm
Initial Adhesion (Adhesion to Steel Ball) ASTM D3759 Test Approximately equivalent to a #3 steel ball
Sustained Adhesion: FTM8 Test ＞24 hours
Temperature Range -40 to 428°F (-40~220°C)
Storage Life 1 year at 73.4°F (23°C) and 60% relative humidity
UL File Number To be determined
UL Test Ribbon OwnLikes VR-30

 

 

 

 

 

 

 

 

 

All SI units are calculated from US customary units.

Why

125um car tire vulcanization label

Excellent high-temperature stability, enduring the heat and pressure (up to 210℃) during tire usage and sulfur treatment.

Outstanding durability and wear resistance.

Excellent chemical resistance: Strong waterproofing, resistant to acids, salts, alkalis, most petroleum stains, oils, and low-fat solvents. The adhesive can penetrate into concave surfaces, firmly bonding with the softening agents that seep out from the tire surface. This ensures that the barcode will not fall off spontaneously during vehicle operation, and forced removal by humans will not damage the tire's rubber surface.

Remarkable barcode/thermal transfer printing effect, combined with OwnLikes V-30 ribbon, ensuring 100% accurate scanning and reading on high-speed conveyors before and after vulcanization.

Excellent conformability: When the tire is removed from the mold, its strong flexibility accommodates tire deformation.

Physical Properties Testing Method Average Test Results
Thickness ASTM D1000 Test US Units Metric Units
Base Material 0.0049 in 0.125 mm
Adhesive 0.0010 in 0.026 mm
Total 0.0059 in 0.151 mm
Initial Tack (Adhesion to Steel Ball) ASTM D3759 Test Approximately equivalent to a 3# steel ball
Sustained Adhesion: FTM8 Test ＞24 hours
Temperature Range -40 to 428°F (-40~220°C)
Storage Life 1 year at 73.4°F (23°C) and 60% relative humidity
UL File Number To be determined
UL Test Ribbon OwnLikes VR-30

 

 

 

 

 

 

 

 

 

All SI units are calculated from US customary units.